王建民,张燕,王艳芳,陈学群.低合金钢中夹杂物对点蚀的影响[J].装备环境工程,2013,10(1):13-16,37. WANG Jian-min,ZHANG Yan,WANG Yan-fang,CHEN Xue-qun.Effect of Inclusions in Low Alloy-steels on Pitting[J].Equipment Environmental Engineering,2013,10(1):13-16,37.
低合金钢中夹杂物对点蚀的影响
Effect of Inclusions in Low Alloy-steels on Pitting
投稿时间:2012-08-19  修订日期:2013-01-01
DOI:
中文关键词:  低合金钢  夹杂物  点蚀
英文关键词:low alloy-steels  inclusions  pitting
基金项目:
作者单位
王建民 海军后勤技术装备研究所,北京100072 
张燕 海军工程质量监督站,北京100161 
王艳芳 海军后勤技术装备研究所,北京100072 
陈学群 海军工程大学,武汉430033 
AuthorInstitution
WANG Jian-min Navy Logistics Technology Equipment Institute,Beijing100072,China 
ZHANG Yan Navy Engineering Quality Suspervision Station,Beijing100161,China 
WANG Yan-fang Navy Logistics Technology Equipment Institute,Beijing100072,China 
CHEN Xue-qun Naval University of Engineering,Wuhan430033,China 
摘要点击次数:
全文下载次数:
中文摘要:
      选择了两种化学成分相似的低合金钢,借助电子探针对其夹杂物做了分析鉴定,通过极化试验、模拟闭塞腐蚀电池试验和显微分析探讨了低合金钢内夹杂物在点蚀过程中的作用。结果表明,低合金钢内夹杂物是最主要的点蚀诱发源,含硫化物的复相夹杂诱发点蚀的能力高于其它夹杂,在点蚀扩展过程中,夹杂物优先溶解脱落形成腐蚀坑,对点蚀扩展有明显促进作用;经钙处理和炉外精炼工艺的低合金钢中夹杂物数量少、体积小,其点蚀点位较高,点蚀扩展速率较低。
英文摘要:
      Two low alloy steels with similar chemical compositions were selected as objects of research. Inclusions in them were analyzed by electronic probe micro-analyzer. The effects of inclusions in low alloy-steels were discussed by polarization tests and simulated occluded corrosion cell combined with microanalysis. The results showed that the inclusions in low alloy-steels are the main pitting initiation and the sulfide inclusions are easier to cause pitting corrosion than other inclusions; inclusions also accelerates pitting corrosion propagation and forms deep pit after dissolving; pitting potential of the alloy-steel by calcium treated and refined secondarily was nobler than that of the steel without because of the less and smaller inclusions; at the same time, pitting propagating rate of the steel treated by calcium and refined secondarily was also less than that of the steel without treatment.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第11717265位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编:400039     电话:023-68792835    Email: zbhjgc@163.com

视频号 公众号