殷宗莲,黄波,胥泽奇,刘杰,张凯.某炮弹底塞表面防护工艺霉菌试验研究[J].装备环境工程,2015,12(4):72-75,94. YIN Zong-lian,HUANG Bo,XU Ze-qi,LIU Jie,ZHANG Kai.Mold Test of Surface Protection Technology for Base Plug of a Type of Bullet[J].Equipment Environmental Engineering,2015,12(4):72-75,94.
某炮弹底塞表面防护工艺霉菌试验研究
Mold Test of Surface Protection Technology for Base Plug of a Type of Bullet
投稿时间：2015-06-05  修订日期：2015-08-15
DOI：10.7643/issn.1672-9242.2015.04.014
中文关键词:  底塞  30CrMnSiNi2A  30CrMnSiA  霉菌试验  防护工艺  润滑脂
英文关键词:base plug  30CrMnSiNi2A  30CrMnSiA  mold test  protection technology  grease
基金项目:
作者单位
殷宗莲 西南技术工程研究所，重庆 400039 
黄波 西南技术工程研究所，重庆 400039 
胥泽奇 西南技术工程研究所，重庆 400039 
刘杰 西南技术工程研究所，重庆 400039 
张凯 西南技术工程研究所，重庆 400039 
AuthorInstitution
YIN Zong-lian Southwest Research Institute of Technology and Engineering，Chongqing 400039，China 
HUANG Bo Southwest Research Institute of Technology and Engineering，Chongqing 400039，China 
XU Ze-qi Southwest Research Institute of Technology and Engineering，Chongqing 400039，China 
LIU Jie Southwest Research Institute of Technology and Engineering，Chongqing 400039，China 
ZHANG Kai Southwest Research Institute of Technology and Engineering，Chongqing 400039，China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究某炮弹底塞最佳表面防护工艺。方法 采用霉菌试验方法， 对2种底塞材料多种表面处理与防护工艺样品的防霉性和防腐蚀性能进行试验和优选。结果 分析了防霉性和防腐蚀性能优劣的原因， 评定出了最优的材料和表面处理与防护工艺组合， 提出了炮弹长贮防霉和防腐蚀的建议和措施。结论 底塞最佳的材料和表面处理与防护工艺组合为30CrMnSiA+镀锌/镀锌镍合金+涂7258号航空润滑油脂。
英文摘要:
      Objective To study the optimal surface protection technology for Base Plug of a type of bullet. Methods Mold test method was used to test the anti-mold property and corrosion resistance of specimens of two kinds of base plug materials processed by different protection technologies. Results The causes for the different corrosion resistance and anti-mold performance was analyzed, the optimal combination of material and surface protection technology was selected, and some suggestions and measures for long storage and corrosion proof of bullets were put forward. Conclusion The optimal material and surface protection technology for base plug of bullet was 30CrMnSiA + galvanizing/zinc-nickel alloy coating + coating with 7258 aviation grease.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第11987659位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编：400039     电话：023-68792835    Email: zbhjgc@163.com

视频号 公众号