付安庆,任越飞,来维亚,徐秀清.天然气管路导气球阀失效分析[J].装备环境工程,2017,14(12):8-13. FU An-qing,REN Yue-fei,LAI Wei-ya,XU Xiu-qing.Failure Analysis on Deflated Ball Valve of Natural Gas Pipeline[J].Equipment Environmental Engineering,2017,14(12):8-13.
天然气管路导气球阀失效分析
Failure Analysis on Deflated Ball Valve of Natural Gas Pipeline
投稿时间:2017-08-17  修订日期:2017-12-15
DOI:10.7643/ issn.1672-9242.2017.12.002
中文关键词:  天然气  球阀  开裂  失效分析
英文关键词:natural gas  ball valve  rupture  failure analysis
基金项目:中石油科学研究与技术研发项目(2017D-2307);国家青年科学基金(21506256)
作者单位
付安庆 石油管材及装备材料服役行为与结构安全国家重点实验室,西安 710077 
任越飞 长庆油田分公司第三采气厂,西安 710018 
来维亚 石油管材及装备材料服役行为与结构安全国家重点实验室,西安 710077 
徐秀清 石油管材及装备材料服役行为与结构安全国家重点实验室,西安 710077 
AuthorInstitution
FU An-qing State Key Laboratory of Performance and Structural Safety for Petroleum Tubular Goods and Equipment Materials, Xi'an 710077, China 
REN Yue-fei The Third Gas Recovery Plant of Chang-qing Oilfield Branch, Xi'an 710018, China 
LAI Wei-ya State Key Laboratory of Performance and Structural Safety for Petroleum Tubular Goods and Equipment Materials, Xi'an 710077, China 
XU Xiu-qing State Key Laboratory of Performance and Structural Safety for Petroleum Tubular Goods and Equipment Materials, Xi'an 710077, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 分析西部某气田天然气管路球阀发生开裂泄漏事故的原因。方法 对球阀的化学成分、断口、金相组织等进行检测分析。结果 球阀裂纹起源于阀体内表面,裂纹沿晶界扩展,晶界未发现贫铬现象,不存在晶间腐蚀;阀体材料存在沿晶铸造缺陷和枝晶露头,水淬激冷过程中形成沿晶微裂纹,承压状态下裂纹沿晶扩展;球阀螺纹根部最薄且应力集中,裂纹由内向外扩展,最终沿螺纹根部环向断裂,断口形貌为沿晶断裂。结论 导气球阀失效原因是螺纹根部存在应力集中和铸造阀体存在缺陷。在两者共同作用下,导致阀体承压状态下沿晶脆性断裂。
英文摘要:
      Objective To analyze causes of the leakage for rupture on ball valve of gas pipeline at a western natural gas field. Methods Chemical composition, fracture and microstructure of the ball valve were analyzed. Results The ball valve cracks originated from the body surface. The cracks extended along the grain boundary. Poor chromium phenomena were not detected in grain boundary and there was no intergranular corrosion. Dendrite and casting defects along grain boundary were found in the material. Micro-cracks formed along grain boundary in the process of water quenching. Cracks propagation was along the grain boundary under pressure. Thread root was the thinnest part and could produce stress concentration. Cracks extended outward and eventually ruptured along the thread root. The fracture morphology was the intergranular brittle fracture. Conclusion The reasons for ball valve failure are the stress concentration in thread root and defects in casting body. Under the effect of both, the intergranular brittle fracture occurs to the valve body under pressure condition.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第11716735位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编:400039     电话:023-68792835    Email: zbhjgc@163.com

视频号 公众号