| 赵连红,张红飞,刘成臣,王浩伟.35Cr2Ni4MoA 材料防腐蚀性能验证研究[J].装备环境工程,2018,15(7):61-65. ZHAO Lian-hong,ZHANG Hong-fei,LIU Cheng-chen,WANG Hao-wei.Verification Research on Corrosion Resistance of 35Cr2Ni4MoA Material[J].Equipment Environmental Engineering,2018,15(7):61-65. |
| 35Cr2Ni4MoA 材料防腐蚀性能验证研究 |
| Verification Research on Corrosion Resistance of 35Cr2Ni4MoA Material |
| 投稿时间：2018-03-27 修订日期：2018-07-25 |
| DOI：10.7643/ issn.1672-9242.2018.07.013 |
| 中文关键词: 35Cr2Ni4MoA 镀硬铬 封孔防护 耐蚀性能 |
| 英文关键词:35Cr2Ni4MoA hard chrome plating sealing protection corrosion resistance |
| 基金项目: |
|
|
| Author | Institution |
| ZHAO Lian-hong | Structure Corrosion Protection and Control of Aviation Science and Technology Key Laboratory, China Special Vehicle Research Institute, Jingmen 448035, China |
| ZHANG Hong-fei | Structure Corrosion Protection and Control of Aviation Science and Technology Key Laboratory, China Special Vehicle Research Institute, Jingmen 448035, China |
| LIU Cheng-chen | Structure Corrosion Protection and Control of Aviation Science and Technology Key Laboratory, China Special Vehicle Research Institute, Jingmen 448035, China |
| WANG Hao-wei | Structure Corrosion Protection and Control of Aviation Science and Technology Key Laboratory, China Special Vehicle Research Institute, Jingmen 448035, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 验证 35Cr2Ni4MoA 材料采取镀硬铬、封孔表面防护的耐腐蚀性能。方法 开展 35Cr2Ni4MoA 材料表面镀硬铬有无封孔防护状态下的实验室加速腐蚀环境试验，研究材料表面腐蚀行为特点，加速腐蚀试验共 8 个周期。通过蚀坑深度、腐蚀面积、单位面积腐蚀数量等描述 35Cr2Ni4MoA 材料表面腐蚀情况。 结果 35Cr2Ni4MoA 材料表面镀硬铬和封孔防护后试验件腐蚀程度明显减低。结论 镀硬铬、封孔表面防护能有效提高海洋环境下 35Cr2Ni4MoA 材料表面的耐蚀性能。 |
| 英文摘要: |
| Objective To verify corrosion resistance of 35Cr2Ni4MoA material which takes hard chrome plating and sealing surface protection. Methods Laboratory accelerated corrosion test of 35Cr2Ni4MoA material which takes surface hard chrome plating was carried out in the presence of sealing protection to study behavior characteristics of surface corrosion. The accelerated corrosion test had 8 cycles. The surface corrosion of 35Cr2Ni4MoA material was described by the depth of corrosion pits, the area of corrosion, the number of corrosion per unit area. Results The corrosion degree of test piece was obviously reduced after hard chrome plating and sealing protection of 35Cr2Ni4MoA material. Conclusion The surface treatment of hard chrome plating and sealing surface protection can effectively improve the surface corrosion resistance of 35Cr2Ni4MoA material under marine environment. |
| 查看全文 查看/发表评论 下载PDF阅读器 |