| 张红飞,赵连红,王浩伟.实验室加速腐蚀环境下7050-T7451厚板疲劳性能研究[J].装备环境工程,2019,16(1):77-81. ZHANG Hong-fei,ZHAO Lian-hong,WANG Hao-wei.Fatigue Properties of 7050-T7451Thick Plate under Accelerated Corrosion Environment in Laboratory[J].Equipment Environmental Engineering,2019,16(1):77-81. |
| 实验室加速腐蚀环境下7050-T7451厚板疲劳性能研究 |
| Fatigue Properties of 7050-T7451Thick Plate under Accelerated Corrosion Environment in Laboratory |
| 投稿时间：2018-07-13 修订日期：2019-01-25 |
| DOI：10.7643/ issn.1672-9242.2019.01.015 |
| 中文关键词: 7050厚板铝合金材料 应力集中系数 腐蚀环境 疲劳性能 |
| 英文关键词:7050 thick plate aluminum alloy material stress concentration coefficient corrosive environment fatigue per-formance |
| 基金项目: |
|
|
|
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究两种应力集中系数7050厚板铝合金材料在腐蚀环境下的腐蚀疲劳性能。方法 开展7050厚板铝合金材料在3.5%NaCl盐水和油箱积水两种环境下的腐蚀疲劳实验，采用三参数式进行S-N曲线拟合分析不同应力集中系数、不同腐蚀环境对7050厚板铝合金材料疲劳性能的影响。结果 腐蚀环境和应力集中系数都会对7050厚板铝合金材料的疲劳性能有影响，3.5%NaCl盐水和油箱积水两种腐蚀环境相较于应力集中系数对于降低材料疲劳性能的影响更大。结论 减少7050厚板铝合金应力集中系数，加强7050厚板铝合金材料腐蚀防护对于提高材料抗疲劳性能有显著作用。 |
| 英文摘要: |
| Objective To study the corrosion fatigue properties of 7050 thick plate aluminum alloy with different stress con-centration coefficient under different corrosion conditions. Methods The corrosion fatigue experiment of 7050 thick plate alu-minum alloy was carried out in 3.5% NaCl salt water and tank water. Influences of different stress concentration coefficient and different corrosion environment on fatigue performance of 7050 thick plate aluminum alloy was analyzed by S-N curve fitting with three parameters. Results Both corrosion environment and stress concentration coefficient had effects on fatigue performance of 7050 thick plate aluminum alloy. The effect of 3.5 % NaCl salt water and tank water on the fatigue performance of the material was greater than that of the stress concentration factor. Conclusion Reducing the stress concentration coefficient of 7050 thick plate aluminum alloy and strengthening the corrosion protection of 7050 thick plate aluminum alloy could improve the fatigue performance of the material significantly. |