| 蒲亚博,王艳艳,刘伟,赵方超,周彩元.某型装备用硅橡胶密封圈热氧老化试验与寿命评估[J].装备环境工程,2022,19(6):52-58. PU Ya-bo,WANG Yan-yan,LIU Wei,ZHAO Fang-chao,ZHOU Cai-yuan.Thermal Oxygen Aging Test and Life Evaluation of Silicone Rubber Seal Ring for a Certain Type of Equipment[J].Equipment Environmental Engineering,2022,19(6):52-58. |
| 某型装备用硅橡胶密封圈热氧老化试验与寿命评估 |
| Thermal Oxygen Aging Test and Life Evaluation of Silicone Rubber Seal Ring for a Certain Type of Equipment |
| |
| DOI：10.7643/issn.1672-9242.2022.06.008 |
| 中文关键词: 橡胶密封圈 热氧老化试验 寿命评估中图分类号:TJ410.89 文献标识码:A 文章编号:1672-9242(2022)06-0052-07 |
| 英文关键词:rubber seal ring thermal oxygen aging test life evaluation |
| 基金项目: |
|
|
| Author | Institution |
| PU Ya-bo | Southwest Technology and Engineering Research Institute, Chongqing 400039, China;Key Laboratory of Ammunition Storage Environmental Effects, China South Industries Group Co., Ltd., Chongqing 400039, China |
| WANG Yan-yan | Southwest Technology and Engineering Research Institute, Chongqing 400039, China;Key Laboratory of Ammunition Storage Environmental Effects, China South Industries Group Co., Ltd., Chongqing 400039, China |
| LIU Wei | Southwest Technology and Engineering Research Institute, Chongqing 400039, China;Key Laboratory of Ammunition Storage Environmental Effects, China South Industries Group Co., Ltd., Chongqing 400039, China |
| ZHAO Fang-chao | Southwest Technology and Engineering Research Institute, Chongqing 400039, China;Key Laboratory of Ammunition Storage Environmental Effects, China South Industries Group Co., Ltd., Chongqing 400039, China |
| ZHOU Cai-yuan | Southwest Technology and Engineering Research Institute, Chongqing 400039, China;Key Laboratory of Ammunition Storage Environmental Effects, China South Industries Group Co., Ltd., Chongqing 400039, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究某型装备用硅橡胶密封圈在温度影响下的性能退化规律，并进行寿命评估。方法 采用热氧老化加速试验方法，试验过程中模拟橡胶密封圈径向承压状态，通过强化温度试验条件，在90、100、110、120 ℃条件下对硅橡胶密封圈进行加速老化试验。以压缩永久变形率作为参数，对试验后的性能检测数据进行分析与处理，结合Arrhenius模型，以硅橡胶(径压)密封圈压缩永久变形率分别达到10%、20%、30%、40%和50%为密封圈失效临界值指标，外推常温25 ℃时硅橡胶密封圈寿命。结果 加速老化试验后，硅橡胶密封圈的压缩变形率逐渐下降，且温度越高，其压缩变形率下降越快。硅橡胶(径压)密封圈在25 ℃条件下，压缩永久变形率达到10%、20%、30%、40%和50%的贮存寿命分别为1、2.9、5.6、9.1、13.8 a。结论 温度是造成硅橡胶密封圈性能退化的因素之一。文中的试验方法和数据处理方法能有效评估〇型密封圈的寿命。 |
| 英文摘要: |
| This paper is to study the performance degradation law of silicone rubber seal ring for a certain type of equipment under the influence of temperature and evaluate its service life.The thermal oxygen aging accelerated test method is adopted to simulate the radial pressure bearing state of the rubber seal ring during the test. The accelerated aging test of the silicone rubber seal ring is carried out at 90, 100, 110 and 120 ℃ by strengthening the temperature test conditions. The performance test data after the test are analyzed and processed with the compression permanent deformation rate as the parameter, combined with the Arrhenius model. Taking the compression permanent deformation rate of silicone rubber (radial pressure) seal ring as 10%, 20%, 30%, 40% and 50% respectively as the critical value index of seal ring failure, the service life of silicone rubber seal ring at 25 ℃ is extrapolated. After the accelerated aging test, the compression deformation rate of silicone rubber seal ring decreases gradually, and the higher the temperature is, the faster the compression deformation rate decreases; at the same time, the storage life of silicone rubber (radial pressure) seal ring with compression permanent deformation rate of 10%, 20%, 30%, 40% and 50% at 25 ℃ is 1, 2.9, 5.6, 9.1 and 13.8 years respectively.Temperature is one of the factors causing the performance degradation of silicone rubber seal ring; the test method and data processing method in this paper can effectively evaluate the service life of O-ring seal. |