| 于谦,侯佳杏,刘劲松,张宏光,刘闯,杨利.浅析盐雾环境对火工药剂安定性能的影响[J].装备环境工程,2022,19(12):40-47. YU Qian,HOU Jia-xing,LIU Jing-song,ZHANG Hong-guang,LIU Chuang,YANG Li.Effects of Salt Spray Environment on Stabilizing Property of Pyrotechnic Agents[J].Equipment Environmental Engineering,2022,19(12):40-47. |
| 浅析盐雾环境对火工药剂安定性能的影响 |
| Effects of Salt Spray Environment on Stabilizing Property of Pyrotechnic Agents |
| |
| DOI：10.7643/issn.1672-9242.2022.12.007 |
| 中文关键词: 火工药剂 盐雾环境 微观形貌 失效机理 热分析技术 本质安定性中图分类号:TJ450 文献标识码:A 文章编号:1672-9242(2022)12-0040-08 |
| 英文关键词:pyrotechnic agents salt spray environment microscopic morphology failure mechanism thermal analysis technology intrinsic stability |
| 基金项目: |
|
|
| Author | Institution |
| YU Qian | Beijing Institute of Technology, Beijing 100081, China |
| HOU Jia-xing | Beijing Institute of Technology, Beijing 100081, China |
| LIU Jing-song | Changchun Institute of Equipment and Process, Changchun 130000, China |
| ZHANG Hong-guang | Changchun Institute of Equipment and Process, Changchun 130000, China |
| LIU Chuang | Changchun Institute of Equipment and Process, Changchun 130000, China |
| YANG Li | Beijing Institute of Technology, Beijing 100081, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 获取海洋生态环境条件下火工药剂性能变化的规律，开展火工药剂在盐雾环境中的安定性试验研究，以保障火工药剂的可靠性。方法 通过SEM成像技术和X–射线衍射技术表征2种典型起爆药叠氮化铅(Lead Azide，LA)和斯蒂芬酸铅(Lead Styphnate，LS)在盐雾试验前后微观形貌及组分的变化，并结合DSC热分析技术，从热分解动力学角度，开展火工药剂在盐雾环境影响下失效机理的研究。结果 在盐雾环境应力的影响下，LA的长柱状晶体结构发生脆化，层裂成不规则的小片状晶型，且随着盐雾试验时间的增加，LA的热分解反应峰会逐渐前移，试验后产物组分只有Pb(OH)Cl，其本质安定性显著下降。LS受盐雾环境应力的影响，其棱柱状晶体结构会层裂为小片状晶型，且部分LS分解形成Pb3(CO3)2(OH)2，导致其安定性降低。结论 2种典型火工药剂LA和LS受盐雾环境应力因素的影响，都会发生失效分解反应，与LA相比，LS在盐雾环境下具有更加稳定的安定性能。 |
| 英文摘要: |
| The work aims to obtain the change rule on the properties of pyrotechnic agents under marine ecological environment, and conduct study about the stability test of pyrotechnic agents in salt spray environment to ensure the reliability of pyrotechnic agents. The microscopic morphology and composition changes of two typical primary explosives, lead azide (LA) and lead styphnate (LS) before and after the salt spray test were characterized by SEM imaging technology and X-ray diffraction technology. The failure mechanism of pyrotechnic agents under the effects of salt spray environment was studied from the perspective of thermal decomposition kinetics by DSC. Under the effects of salt spray environmental stress, the long columnar crystal structure of LA was embrittled and cracked into irregular small flaky crystals. Moreover, the thermal decomposition reaction peak of LA gradually moved forward with the increase of salt spray test time. After the test, the product component was Pb(OH)Cl, and its intrinsic stability decreased; Under the effects of salt spray environmental stress, its prismatic crystal structure was stratified into small flake crystal, and part of LS decomposed into Pb3(CO3)2(OH)2, resulting in a significant decrease on its intrinsic stability. Two typical pyrotechnic agents, LA and LS, are affected by the stress factors of the salt spray environment, and both will undergo failure decomposition reactions. Compared with LA, LS is more stable in the salt spray environment. |