王雁涛,杨钿.铝合金结构件应力腐蚀裂纹机理分析[J].装备环境工程,2013,10(1):53-56. WANG Yan-tao,YANG Tian.Analysis on Stress Corrosion CrackMechanisms of Aluminum Alloy Structure[J].Equipment Environmental Engineering,2013,10(1):53-56.
铝合金结构件应力腐蚀裂纹机理分析
Analysis on Stress Corrosion CrackMechanisms of Aluminum Alloy Structure
投稿时间:2012-11-07  修订日期:2013-01-01
DOI:
中文关键词:  铝合金  应力腐蚀  裂纹  机理
英文关键词:aluminum alloy  stress corrosion  crack  mechanism
基金项目:
作者单位
王雁涛 海军装备部驻重庆地区军事代表局,重庆400042 
杨钿 总装备部驻重庆地区军事代表局,重庆400060 
AuthorInstitution
WANG Yan-tao Military Representative Bureau of Naval Equipment Department in Chongqing Region,Chongqing400042,China 
YANG Tian Military Representative Bureau of General Equipment Department in Chongqing Region,Chongqing400060,China 
摘要点击次数:
全文下载次数:
中文摘要:
      舰船电子装备铝合金结构件在焊接加工、安装中余留了大量应力,并且长期工作于恶劣的腐蚀环境,导致出现应力腐蚀裂纹,使结构件强度或密闭性严重降低。分析了应力腐蚀裂纹发生的原因,提出了工艺控制及改进的措施。
英文摘要:
      There exist large amount of residual stresses when aluminum alloy structures of electronic equipments are welded and installed. Furthermore, stress corrosion cracks on the structures may emerge due to long period of working under serious corrosion environment, which makes the structure strength and impermeability severely drop. The causes for stress corrosion cracks of the aluminum alloy structures were analyzed. Some process control and improvement measures were put forward.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13538415位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编:400039     电话:023-68792835    Email: zbhjgc@163.com

视频号 公众号