曹付齐,李小换,刘志成,李彦丽,韵胜.某推进剂低温加速老化试验研究[J].装备环境工程,2014,11(4):88-92. CAO Fu-qi,LI Xiao-huan,LIU Zhi-cheng,LI Yan-li,YUN Sheng.Low-temperature Accelerated Aging Study of a Propellant[J].Equipment Environmental Engineering,2014,11(4):88-92.
某推进剂低温加速老化试验研究
Low-temperature Accelerated Aging Study of a Propellant
投稿时间:2014-03-11  修订日期:2014-04-15
DOI:10.7643/issn.1672-9242.2014.04.017
中文关键词:  推进剂  老化  力学性能
英文关键词:propellant  aging  mechanical properties
基金项目:
作者单位
曹付齐 中国空空导弹研究院, 河南 洛阳 471009 
李小换 中国空空导弹研究院, 河南 洛阳 471009 
刘志成 空军驻包头地区军代室, 呼和浩特 010010 
李彦丽 航天科工六院 46 所, 呼和浩特 010010 
韵胜 航天科工六院 46 所, 呼和浩特 010010 
AuthorInstitution
CAO Fu-qi China Airborne Missile Academy, Luoyang 471009, China 
LI Xiao-huan China Airborne Missile Academy, Luoyang 471009, China 
LIU Zhi-cheng Air Force Military Representative Office in Baotou, Huhhot 010010, China 
LI Yan-li The 46th Institute of the Sixth Academy of CASIC, Huhhot 010010, China 
YUN Sheng The 46th Institute of the Sixth Academy of CASIC, Huhhot 010010, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 考查某推进剂在-10 ℃ 和-28 ℃ 这两个温度下性能随老化时间的变化趋势。 方法 采用低温加速老化试验。 结果 在低温下老化推进剂最大抗拉强度先下降然后逐渐升高,伸长率变化趋势较为复杂。 常温正常拉伸速度条件下伸长率基本在初始值附近波动,低温快速拉伸条件下伸长率直线下降。 结论 低温下推进剂老化力学性能的变化趋势与高温老化不尽相同,造成这种差异的原因可能是老化机理不同所致。
英文摘要:
      Objective To study the characteristic changing trends of a propellant at-10 ℃ and-28 ℃ . Methods Lowtemperature accelerated aging test method was used. Results At low temperature, the maximum tensile strength of the aging propellant first decreased and then gradually increased. The changing trend of elongation rate was quite complicated. At room temperature and normal tensile speed, the elongation rate fluctuated around the initial value, while at low temperature and rapid tensile, the elongation rate showed linear decrease. Conclusion The changing trends of mechanical properties seemed different during aging at low or high temperature, the cause of which might be the different aging mechanism.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第12861389位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编:400039     电话:023-68792835    Email: zbhjgc@163.com

视频号 公众号