田骏,李国明,陈珊.Si对低合金钢耐海水腐蚀性能影响的电化学研究[J].装备环境工程,2016,13(2):110-115. TIAN Jun,LI Guo-ming,CHEN Shan.Electrochemical Study on Effects of Si Contents on the Corrosion Resistance of Low Alloy Steels to Sea Water[J].Equipment Environmental Engineering,2016,13(2):110-115.
Si对低合金钢耐海水腐蚀性能影响的电化学研究
Electrochemical Study on Effects of Si Contents on the Corrosion Resistance of Low Alloy Steels to Sea Water
投稿时间:2015-09-17  修订日期:2016-04-15
DOI:10.7643/issn.1672-9242.2016.02.020
中文关键词:  Si  低合金钢  电化学性能  海水腐蚀
英文关键词:Si  low alloy steel  electrochemical properties  sea water corrosion
基金项目:
作者单位
田骏 海军工程大学,武汉 430033 
李国明 海军工程大学,武汉 430033 
陈珊 海军工程大学,武汉 430033 
AuthorInstitution
TIAN Jun Naval University of Engineering,Wuhan 430033,China 
LI Guo-ming Naval University of Engineering,Wuhan 430033,China 
CHEN Shan Naval University of Engineering,Wuhan 430033,China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究Si对低合金钢耐海水腐蚀性能的影响。方法 采用真空电弧炉冶炼了不同硅含量的低合金钢, 通过极化试验研究钢在海水中的腐蚀特性。采用交流阻抗和线性极化研究锈层对钢的保护作用, 并对夹杂物进行SEM及EDAX分析。结果 当硅的质量分数小于0.9%时, 其在海水中的腐蚀速度随硅的质量分数增加而增加; 当硅的质量分数大于0.9%时, 其在海水中的腐蚀速度随硅含量的增加而减小。随浸泡时间延长, 钢的耐蚀性降低。结论 Si的质量分数为0.9%时, 钢耐蚀性的最好, 锈层对钢的腐蚀不具有保护作用。
英文摘要:
      Objective To study the effect of Si on the resistance of low alloy steel to sea water corrosion by electrochemical methods. Methods Low alloy steels with different mass fractions of Si were smelted by vacuum arc furnace. The corrosion resistance of the steel in sea water was evaluated by polarization tests. The corrosion resistance of the rust layer after full immersion was studied by linear polarization test and EIS test. The composition of inclusions was studied by scanning electron microscopy (SEM) and energy dispersive analysis of X-ray (EDAX). Results The experiment results indicated that when the Si content was less than 0.9%, the uniform corrosion rate increased with the increase of Si content; when the Si content was more than 0.9%, the corrosion rate decreased with increasing content of Si; the corrosion resistance of the steel decreased as the time of immersion prolonged. Conclusion When the Si content was 0.9%, the steel had the best corrosion resistance; the protection ability of rust layer was limited.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13491603位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编:400039     电话:023-68792835    Email: zbhjgc@163.com

视频号 公众号