王玲,赵全成,杨万均.海洋大气环境对铝合金电连接器壳体腐蚀及电气性能影响[J].装备环境工程,2019,16(5):85-89. WANG Ling,ZHAO Quan-cheng,YANG Wan-jun.Effects of Marine Atmospheric Environment on Corrosion and Electrical Performance of Aluminum Alloy Electrical Connector Shell[J].Equipment Environmental Engineering,2019,16(5):85-89.
海洋大气环境对铝合金电连接器壳体腐蚀及电气性能影响
Effects of Marine Atmospheric Environment on Corrosion and Electrical Performance of Aluminum Alloy Electrical Connector Shell
投稿时间:2018-12-23  修订日期:2019-05-25
DOI:10.7643/ issn.1672-9242.2019.05.016
中文关键词:  铝合金  电连接器  海洋环境  腐蚀  电气性能
英文关键词:aluminum alloy  electrical connectors  marine environment  corrosion  electrical properties
基金项目:
作者单位
王玲 西南技术工程研究所 国防科技工业自然环境试验研究中心,重庆 400039 
赵全成 西南技术工程研究所 国防科技工业自然环境试验研究中心,重庆 400039 
杨万均 西南技术工程研究所 国防科技工业自然环境试验研究中心,重庆 400039 
AuthorInstitution
WANG Ling Natural Environmental Test and Research Center of Science, Southwest Technology and Engineering Research Institute, Chongqing 400039, China 
ZHAO Quan-cheng Natural Environmental Test and Research Center of Science, Southwest Technology and Engineering Research Institute, Chongqing 400039, China 
YANG Wan-jun Natural Environmental Test and Research Center of Science, Southwest Technology and Engineering Research Institute, Chongqing 400039, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究海洋大气环境对2A12和6061铝合金电连接器性能的影响。方法 开展2A12和6061铝合金电连接器在海南万宁试验站4 a棚下暴露试验,通过宏微观形貌观察和电气性能测试对比分析两种铝合金电连接器壳体的腐蚀差异和电气性能变化。结果 两种铝合金电连接器壳体均出现镀层鼓泡、剥落和基体腐蚀,6061铝合金电连接器壳体腐蚀程度高于2A12铝合金电连接器。2A12铝合金基体发生点蚀和晶间腐蚀,6061铝合金基体发生剥蚀,基体腐蚀产物堆积,导致镀镍层开裂剥落,进而失去防护作用。相对于导通性能、耐压强度,电连接器的绝缘电阻对海洋大气环境更为敏感。结论 铝合金化学镀镍壳体电连接器在热带海洋大气环境下不适宜长期使用。
英文摘要:
      Objective To study the effects of marine atmospheric environment on performance of 2A12 and 6061 aluminum alloy electrical connectors. Methods Atmospheric environment test of 2A12 and 6061 aluminum alloy electrical connectors were carried out in Wanning Test Station for 4 a. Corrosion difference and change of electrical properties of two kinds of aluminum alloy electrical connectors were analyzed by morphology observation and electrical performance test. Results Coating bubbling, spalling and matrix corrosion occurred in the shell of two kinds of aluminum alloy electrical connectors. The corrosion degree of 6061 aluminum alloy electrical connector shell was higher than that of 2A12 aluminum alloy. Pitting corrosion and intergranular corrosion occurred in 2A12 aluminum alloy base, and corrosion occurred in 6061 aluminum alloy base. The accumulation of corrosion products resulted in cracking and spalling of nickel plating layer. Compared with continuity and compression strength, the insulation resistance of electrical connectors was more sensitive to marine atmosphere environment. Conclusion Electrical connectors of electroless nickel-plated aluminum alloy shell are unsuitable for long-term use in tropical marine atmospheric environment.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13538574位访问者    渝ICP备15012534号-5

版权所有:《装备环境工程》编辑部 2014 All Rights Reserved

邮编:400039     电话:023-68792835    Email: zbhjgc@163.com

视频号 公众号